The following are test results from Dr. William C. LaCourse, Professor of Glass Science at the Institute for Glass Science and Engineering at Alfred University, New York, an independent testing laboratory. Dr. LaCourse is an expert in the study of glass and ceramics. He has done testing for major companies like PPG and Kohler. Below is a summary of the most important findings of his tests.

Dr. LaCourse states in his reports that our improved process has a remarkably low coefficient of friction when the glass is wet. He states that when glass is wet, it is by far the "most dangerous period" with regards to the potential for damage. The report says that "we believe that the (main) usefulness of your coating lies in its maintenance of a low friction coating over the life of the glass". Below is a formula that puts into layman's terms the results of the coefficient of friction tests.

Contact Angle Untreated Glass Treated with Diamon-Fusion (DF1- Step #1) Treated with Diamon-Fusion (DF2- Step #2)

Contact angle: Contact angle is the scientific method of measuring the water repellency of a surface. The higher the number, the higher the water repellency of the surface. Material Angle Contact Angle Untreated Glass 14° Improved Diamon-Fusion® 106° Our main competitor 91° The latest improvement of the Diamon-Fusion technology has an additional 2nd step that creates the 'capping' (in the chain of atoms) which changes the molecular composition of the treated surface. (Since Dr. Lacourse ran these tests the process has been improved again and now it consistently tests out at 116°-118°)

Coefficient of Friction: (with Glass indentor wet) Material µ Untreated Glass 0.82 Improved Diamon-Fusion®  0.13

To make the test results for coefficient of friction useful, we have used a formula that translates the data into the force required to cause damage to the surface. Assume that a load of 10 lbs. has been placed on the rider under static conditions, and that this is the lowest load that caused cracking (no dragging). Using the formula we can now calculate the load that would cause cracking to occur when the rider is dragged across the sample.

back to top

Load required to damage surface:

Note that when comparing wet vs. wet friction calculations indicate that it would take more than 10 times the load (4.0 lbs. vs. 0.37 lbs.) to cause damage on your treated sample vs. the untreated.

In other words, the weight of a debris particle required to crack a piece of glass that has been treated with Diamon-Fusion® would need to be ten times heavier than the weight required to crack an untreated piece of glass.

B-B GUN TEST

This piece of 10 mm Clear Laminated Glass was treated on the left side only and shot 20 times, alternating sides, with an air powered B-B gun from 16 metres. The amazing results show:

(a) While the treated side may be damaged, the majority of the shots bounced off with no damage and the only break is considered to be a "repairable" break by most windshield repair companies.

(b) The untreated side, on the other hand, broke almost every time with the majority of the breaks not being repairable.Our competitors can't say this!

__________________________________________________________________________________________

University Tests

The following are test results from Dr. William C. LaCourse, Professor of Glass Science at the Institute for Glass Science and Engineering at Alfred University, New York, an independent testing laboratory. Dr. LaCourse is an expert in the study of glass and ceramics. He has done testing for major companies like PPG and Kohler. Below is a summary of the most important findings of his tests.

Dr. LaCourse states in his reports that our improved process has a remarkably low coefficient of friction when the glass is wet. He states that when glass is wet, it is by far the "most dangerous period" with regards to the potential for damage. The report says that "we believe that the (main) usefulness of your coating lies in its maintenance of a low friction coating over the life of the glass". Below is a formula that puts into layman's terms the results of the coefficient of friction tests.

Contact Angle Untreated Glass Treated with Diamon-Fusion (DF1- Step #1) Treated with Diamon-Fusion (DF2- Step #2)

Contact angle: Contact angle is the scientific method of measuring the water repellency of a surface. The higher the number, the higher the water repellency of the surface. Material Angle Contact Angle Untreated Glass 14° Improved Diamon-Fusion® 106° Our main competitor 91° The latest improvement of the Diamon-Fusion technology has an additional 2nd step that creates the 'capping' (in the chain of atoms) which changes the molecular composition of the treated surface. (Since Dr. Lacourse ran these tests the process has been improved again and now it consistently tests out at 116°-118°)

Coefficient of Friction: (with Glass indentor wet) Material µ Untreated Glass 0.82 Improved Diamon-Fusion®  0.13

To make the test results for coefficient of friction useful, we have used a formula that translates the data into the force required to cause damage to the surface. Assume that a load of 10 lbs. has been placed on the rider under static conditions, and that this is the lowest load that caused cracking (no dragging). Using the formula we can now calculate the load that would cause cracking to occur when the rider is dragged across the sample.

back to top

Load required to damage surface:

Note that when comparing wet vs. wet friction calculations indicate that it would take more than 10 times the load (4.0 lbs. vs. 0.37 lbs.) to cause damage on your treated sample vs. the untreated.

In other words, the weight of a debris particle required to crack a piece of glass that has been treated with Diamon-Fusion® would need to be ten times heavier than the weight required to crack an untreated piece of glass.